Development of Laminated Planks made from Bolo Gi antochloa levis Bamboo
Reyes, Angelie Marie C.
Development of Laminated Planks made from Bolo Gi antochloa levis Bamboo [manuscript] / Angelie Marie C. Reyes. - Magalang, Pampanga : Pampanga State Agricultural University, August 2022. - xiv, 57 leaves ; 28 cm. + 1 computer disc (4 3/4 in.)
The study aimed to develop laminated planks from Bolo (Gigantochloa levis) bamboo. Processes in developing laminated bamboo planks are drying, splitting, planing, laminating and subjecting to heat press. Three different binders were used for the laminating process which includes polyvinyl acetate, construction adhesive and animal glue. The average amount of water absorbed by laminated bamboo planks is 21.37% while the mean burned area during fire resistance test is 95.36 cm*. Compressive and flexural strength was also obtained in this study which ranges from 1.30-1.74 MPa and 79.51-158.42 MPa, respectively. In terms of appearance and properties, polyviny! acetate has achieved the highest rating using likert scale. Overall findings of the study revealed that the polyvinyl acetate is the most suitable adhesive for laminated bamboo planks among all thThe study aimed to develop laminated planks from Bolo (Gigantochloa levis) bamboo. Processes in developing laminated bamboo planks are drying, splitting, planing, laminating and subjecting to heat press. Three different binders were used for the laminating process which includes polyvinyl acetate, construction adhesive and animal glue. The average amount of water absorbed by laminated bamboo planks is 21.37% while the mean burned area during fire resistance test is 95.36 cm*. Compressive and flexural strength was also obtained in this study which ranges from 1.30-1.74 MPa and 79.51-158.42 MPa, respectively. In terms of appearance and properties, polyviny! acetate has achieved the highest rating using likert scale. Overall findings of the study revealed that the polyvinyl acetate is the most suitable adhesive for laminated bamboo planks among all the adhesive used. e adhesive used.
Development of Laminated Planks made from Bolo Gi antochloa levis Bamboo [manuscript] / Angelie Marie C. Reyes. - Magalang, Pampanga : Pampanga State Agricultural University, August 2022. - xiv, 57 leaves ; 28 cm. + 1 computer disc (4 3/4 in.)
The study aimed to develop laminated planks from Bolo (Gigantochloa levis) bamboo. Processes in developing laminated bamboo planks are drying, splitting, planing, laminating and subjecting to heat press. Three different binders were used for the laminating process which includes polyvinyl acetate, construction adhesive and animal glue. The average amount of water absorbed by laminated bamboo planks is 21.37% while the mean burned area during fire resistance test is 95.36 cm*. Compressive and flexural strength was also obtained in this study which ranges from 1.30-1.74 MPa and 79.51-158.42 MPa, respectively. In terms of appearance and properties, polyviny! acetate has achieved the highest rating using likert scale. Overall findings of the study revealed that the polyvinyl acetate is the most suitable adhesive for laminated bamboo planks among all thThe study aimed to develop laminated planks from Bolo (Gigantochloa levis) bamboo. Processes in developing laminated bamboo planks are drying, splitting, planing, laminating and subjecting to heat press. Three different binders were used for the laminating process which includes polyvinyl acetate, construction adhesive and animal glue. The average amount of water absorbed by laminated bamboo planks is 21.37% while the mean burned area during fire resistance test is 95.36 cm*. Compressive and flexural strength was also obtained in this study which ranges from 1.30-1.74 MPa and 79.51-158.42 MPa, respectively. In terms of appearance and properties, polyviny! acetate has achieved the highest rating using likert scale. Overall findings of the study revealed that the polyvinyl acetate is the most suitable adhesive for laminated bamboo planks among all the adhesive used. e adhesive used.